The method of reducing the self-explosion of tempered glass！

1. Flat glass is preferred. High-quality flat glass has low content of stones, bubbles, impurities and nickel sulfide. Using high-quality flat glass as the original sheet for making tempered glass can significantly reduce the self-explosion of tempered glass. 

2. Improve the edge processing quality of tempered glass to avoid scratches and bumps on the edge and surface of the glass. 

3. Improve the stress uniformity and symmetry along the thickness direction of the tempered glass surface. 

4. Explore the possibility of lowering the limit of compressive stress indicated by tempered glass. 

5. Increase the application amount of homogenized tempered glass, and study the method of detecting the homogeneity of tempered glass, so that the homogenization process starts. 

6. Reducing the total application of tempered glass and increasing the application of semi-tempered glass and laminated glass can reduce the number of self-explosions of tempered glass. It goes without saying that the total amount of tempered glass applications is reduced, and the number of self-explosions of tempered glass must be reduced. 

7. Reducing the size of the tempered glass panel can reduce the self-explosion rate of the tempered glass. The larger the size of the tempered glass and the thicker the glass plate, the greater the probability of self-explosion. 

8. In practical projects, the area of use of tempered glass is getting larger and larger. For tempered glass with a large surface, not only the relative value of its curvature, but also the absolute value of its curvature should be required to reduce the assembly of tempered glass. stress to avoid self-explosion of tempered glass after long-term use.